台灣.新竹縣湖口鄉新竹工業區光復路71號
+886-3-597-8899

一般型

一般型
General Type
產品
說明書
品名
Articles
固成份
NV %
粘 度
Viscosity
(cps/25℃)
溶劑
Solvents
NCO含量
%
特性及應用
Characteristics & Applications
CL-502 75±2 4000 ~ 8000 EAC 12.7~13.3 無色 , 一般型
Clear, general type.
CL-502R 75±2 3000 ~ 5000 EAC 12.7~13.3 淺藍色 , 一般型
Slight blue color, general type.
CL-5775 70±2 250 ~ 600 TO 8.1-8.8 壓克力樹脂用架橋劑
Cross-linking agents for Acrylic resins.
CL-5775 75±2 500 ~ 1500 TO 8.5 - 9.4 壓克力樹脂用架橋劑
Cross-linking agents for Acrylic resins.
CL-5775L 71~75 500~750 TO 8.7~9.6 壓克力樹脂用架橋劑
Cross-linking agents for Acrylic resins.
CL-503 40±2 10~50 EAC
DMC
or TO
6.2~6.8 硬度高,耐化性佳,可作為木器之二液型底漆、面漆等,易砂磨
high hardness, excellent solvent resistance. Hardener of two-component PU resins for wood coating, easily to be polished.
CL-503 50±2 30 ~ 120 EAC
DMC
or TO
7.6 – 8.2 硬度高,耐化性佳,可作為木器之二液型底漆、面漆等,易砂磨
high hardness, excellent solvent resistance. Hardener of two-component PU resins for wood coating, easily to be polished.
CL-503 55±2 120 ~ 250 EAC
DMC
or TO
8.3 - 8.9 硬度高,耐化性佳,可作為木器之二液型底漆、面漆等,易砂磨
high hardness, excellent solvent resistance. Hardener of two-component PU resins for wood coating, easily to be polished.
CL-503 60±2 250 ~ 700 EAC
DMC
or TO
9.1 - 9.7 硬度高,耐化性佳,可作為木器之二液型底漆、面漆等,易砂磨
high hardness, excellent solvent resistance. Hardener of two-component PU resins for wood coating, easily to be polished.
CL-503 65±2 900 ~ 2000 EAC
DMC
or TO
9.8 - 10.5 硬度高,耐化性佳,可作為木器之二液型底漆、面漆等,易砂磨
high hardness, excellent solvent resistance. Hardener of two-component PU resins for wood coating, easily to be polished.
CL-503 70±2 3000~7000 EAC
DMC
or TO
10.5 - 11.5 硬度高,耐化性佳,可作為木器之二液型底漆、面漆等,易砂磨
high hardness, excellent solvent resistance. Hardener of two-component PU resins for wood coating, easily to be polished.
CL-503 75±2 3700~7700 EAC
DMC
or TO
11.9 - 12.5 硬度高,耐化性佳,可作為木器之二液型底漆、面漆等,易砂磨
high hardness, excellent solvent resistance. Hardener of two-component PU resins for wood coating, easily to be polished.
CL-503D 75±2 2000~5000 EAC 12.1~12.6 淡黃透明色,一般型
Slight yellow color, General type.
CL-503G 75±2 20000~30000 EAC 11.4~12.0 硬度高,耐化性佳,可作為木器之二液型底漆、面漆等,易砂磨
high hardness, excellent solvent resistance. Hardener of two-component PU resins for wood coating, easily to be polished.
CL-503T 75±2 3000~7000 EAC 12.5-13 硬度高,耐化性佳,可作為木器之二液型底漆、面漆等,易砂磨
high hardness, excellent solvent resistance. Hardener of two-component PU resins for wood coating, easily to be polished.